What Is Multi Jet Fusion (MJF)?

Multi Jet Fusion (MJF) is a powder-bed 3D printing process developed by HP that bonds agent and powder in a process similar to binder jetting. Unlike point-by-point laser-based powder-bed fusion systems, MJF selectively distributes fusing and detailing agents across a bed of powder, and layers are fused together using infrared light.

The Multi Jet Fusion system consists of exchangeable build units that can be wheeled between MJF 3D printers and separate postprocessing stations for rapid cooldown and powder removal. This modular system enables the printer and postprocessing stations to run continuously while build units cycle through, speeding part production.

How Does Multi Jet Fusion Work?

The Multi Jet Fusion printhead deposits droplets of binding and detailing agents across layers of polymer powder in a preheated bed. The binder serves as a heat-absorbing ink, making the powder it binds more prone to melting. Each layer is fused using infrared light to melt the areas held by the binding agent all at once. Meanwhile, the detailing agent enables a cooling effect, providing crisp edges around the melted area and preventing the meltpool from bleeding into the loose powder. Powder is distributed on top of each solid layer, and the process repeats until the part is complete. The powder supports the parts as they grow; support structures are not necessary, which enables greater design freedom and enables larger quantities to be produced at once.

What Postprocessing Is Required?

When the build finishes, the build unit (the entire powder bed with the encapsulated parts) is removed from the printer and placed into the postprocessing unit for rapid cooling. Then the build unit is moved to a processing station where loose powder is removed by vacuum.

Final parts are said to have quality surface finishes, fine feature resolution and ‬more consistent mechanical properties when compared to laser-based powder bed processes like selective laser sintering (SLS). And, because heating takes place layer by layer with powder packed beneath the parts, warping occurs less with MJF than with SLS.

To improve surface finish, parts can be bead blasted, then given a primer finish or a paint finish. Printed parts can be dyed or treated further if required for the application.

What Materials Can Be Used?

Multi Jet Fusion is compatible with a selection of thermoplastics from HP, including High Reusability (HR) PA 12 nylon, HR PA 12 GB (a nylon reinforced with glass beads) and HR PA 11.

HP also supports a 3D Materials Certification Program and has partnered with polymer 3D printing material suppliers to develop new materials. Material partners include Arkema, BASF, Dressler Group, Evonik, Henkel, Lehmann & Voss & Co., Lubrizol and Sigma Design.

Why Use Multi Jet Fusion?

Multi Jet Fusion can produce functional prototypes and end-use production parts in as fast as one day. A single MJF printer has the ability to run almost continuously if the build units are swapped out for postprocessing as each print is completed. Used powder can be recycled by loading it back into a build unit from the postprocessing station.

The layer-by-layer fusion of MJF enables the process to be faster than point-by-point 3D printing systems, and each layer is said to take the same amount of time to fuse regardless of complexity. With MJF it is possible to nest parts vertically as well as horizontally, filling the entire build volume with individual, separate parts. Multi Jet Fusion requires no tooling investment or minimum order volume; these factors combined with its speed make the process competitive with injection molding for serial production.